ABS-like Carbon RPU 70
A tough all-purpose engineering grade material that comes in black.
Product Description
RPU 70 Rigid Polyurethane is manufactured through Carbon’s DLS (digital light synthesis) process. It is a tough all-purpose engineering grade material that comes in black and can be categorized as an ABS-like materials. Ideal part sizes for Carbon materials are 5 in. x 5 in. x 5 in. or less.
Applications
- Complex designs that are challenging to mold
- Production parts
- Durable end-use components
Key Benefits
- Toughness
- UL 94 HB flame resistance classification
Related Materials
- Carbon FPU 50
- Carbon EPX 86Fr
ABS-like Carbon RPU 70 Properties
The following mechanical, electrical, and thermal property data was gathered from the base material used
in the formulation of MicroFine material. Properties of the final formulated material may differ from those
published below.
General Properties
| Value | |
|---|---|
| Hardness, ASTM D2240 | 80, Shore D |
| Density, ASTM D792 | 1.08 g/cm3 |
| Density (liquid resin) | 1.01 g/cm3 |
| Taber Abrasion, ASTM D4060, CS-17, 1 kg, 100% vacuum | 70 mg / 1000 cycles |
| Water Absorption, Short Term (24 hours) ASTM D570 | < 0.5% |
| Water Absorption, Long Term (14 days) ASTM D570 | < 1.5% |
Tensile Properties
ASTM D638, Type V, 10 mm/min
| Metric | US | |
|---|---|---|
| Tensile Modulus | 1700 MPa | 245 ksi |
| Yield Strength | 40 MPa | 6 ksi |
| Strain at Yield | 5% | 5% |
| Ultimate Tensile Strength | 40 MPa | 6 ksi |
| Elongation at Break | 100% | 100% |
Carbon DLS Finishing Options
Unfinished
With unfinished, you get varying aesthetics based on build orientation. Dots or standing nibs remain evident on the bottom of the part from the support structure remnants.
Natural Finish
With natural finishing, you get varying aesthetics based on build orientation. Standing nibs are sanded flat.