Accura 5530 3D Printing Material
Accura 5530 is a high temperature resistant material available for SLA 3D printing.
Product Description
PC-Like Translucent (Advanced High Temp) or Accura 5530 is best used for parts that need strength and stiffness combined with high temperature resistance. With a thermal post-cure, the part’s heat deflection can be improved even further, but at the expense of durability.
Applications
Advanced PC-Like High-Temp Translucent works well for parts that require high temperature resistance such as under-the-hood-automotive or electrical components.
Tolerances
For well-designed parts, tolerances in the X/Y dimension of ±0.002 in. (0.05mm) for the first inch plus ±0.001 in./in., and Z-dimension tolerances of ±0.005 in. (0.127mm) for the first inch plus ±0.001 in./in. (0.001mm/mm), can typically be achieved.
Note that tolerances may change depending on part geometry.
Key Product Benefits
- High temperature resistance
- Higher resistance to heated fluids
- Translucent
Related Materials
- PC-Like Translucent (Accura 60)
- ABS-like Gray (Accura Xtreme Gray)
- ABS-like Black (Accura 7820)
- MicroFine™ (Gray and Green)
PC-like Translucent Advanced High Temp (Accura 5530) Properties
All of the figures contained on this data sheet are approximate and dependent on a number of factors, including but not limited to, machine and process parameters. The information provided is therefore not binding and not deemed to be certified.
| Property | Test Method | Value | After Optional Thermal Post-Curing |
|---|---|---|---|
| Color | - | Light Tan | Amber |
| Density in solid state* | @ 25 °C (77 °F) | 1.21 g/cm³ | - |
| Water Absorption (20 °C, 50% relative humidity) | ASTM D570 | 0.55 ± 0.15% | 0.55 ± 0.15% |
| E-module (x-y plane) | ASTM D638, test speed 10mm/min | 3,400 ± 400 MPa | 3,900 ± 400 MPa |
| Tensile strength (x-y plane) | ASTM D638, test speed 10mm/min | 50 ± 10 MPa | 45 ± 10 MPa |
| Elongation at break (x-y plane) | ASTM D638, test speed 10mm/min | 3 ± 2% | 1.5 ± 1% |
| Heat deflection temperature @ 0.46 MPa* | ASTM D648 | 70 – 85 °C (158 – 185 °F) | 170 – 250 °C (338 – 482 °F) |
| Heat deflection temperature @ 1.82 MPa* | ASTM D648 | 55 – 58 °C (131 – 136 °F) | 110 – 120 °C (230 – 248 °F) |
* From supplier data sheet